Epichlorohydrin Rubber Binary Polymer

Tensile strength at break Tb （Mpa)

13.5

Elongation at break Eb （%）

410

Heat resistance of aging 150℃×72hrs

Hardness (shore A)

-1

Change rate of tensile strength at break Tb （%)

-21

Change rate of elongation at break Eb （%）

-43

Compression set (%)

125℃×72hrs 30%

39

Resistance to 903# oi 125℃×72hrs

Hardness (shore A)

-1.5

Change rate of tensile strength at break Tb （%)

-5.6

Change rate of elongation at break Eb （%）

-2.1

Volume change △V （%）

3.1

Resistance to fuel C 40℃×48hrs

Volume change △V （%）

43

Cold resistance

Bending fracture temperature T   (℃)

-42