| Material: | PTFE | ||
|---|---|---|---|
| High Light: | Paints PTFE Micro Powder,PTFE Micro Powder JH-310,2uM PTFE Powder |
||
Product introduction
JH-310 is a polytetrafluoroethylene white powder prepared by a special method, with very low molecular weight of 5000-10000. The particle size of this product is extremely small which is suitable for customers who have higher requirements of particle size distribution. JH-310 not only maintains all the original excellent properties of PTFE, but also has many unique properties, such as no self-aggregation, good compatibility, good dispersion, high self-lubricating property, and significantly reduced friction coefficient.
JH-310 can be used alone as a solid lubricant, or as an additive for plastics, rubber, paint, ink, lubricating oil, grease, etc. Various typical powder processing methods can be used when mixing with plastic or rubber, such as blending, etc., and the addition amount is 5-20%; when used in lubricating oil and grease, it can increase the viscosity and reduce the friction coefficient of the Substrate
.
JH-310 is usually used as a processing aid, and can also be used alone as a lubricant. But it cannot be used to replace high molecular weight PTFE suspension or dispersion resin for extrusion or compression molding.
Technical Data
| Item | Unit | Index | Test Method |
| D50(average particle size) | μm | 1.5-2.0 | ASTM D4464 |
| D90(maximum particle size) | μm | ≤5.0 | ASTM D4464 |
| Melting Point | °C | 325±5 | ASTM D4591 |
| Specific Surface Area | M2/g | 6.45 | ASTM D5675 |
| Water Content (%) | ≤0.05 | 150°C/2h | |
| Specific Gravity | g/cc | 2.1-2.2 | ASTM D5675 |
| Appearance | White powder | Visual inspection |
Main Application
JH-310 is mainly used in paints, coatings, printing inks, lubricating greases and other fields, and can be used to improve the friction resistance, surface smoothness and non-stick properties of products.
Dosage and usage
In different systems, the amount of JH-310 added is generally between 0.5wt% and 3.0wt%.
Usually, it can be added through grinding, ball milling, three-roll grinding machines or high-shear dispersing equipment, and high-speed stirring at 1600 rpm. At the same time, when adding micro-powder, it should be added in a small amount for several times or made into wax slurry to make the micro-powder fully wet.
Package and transportation
Composite paper drum packaging, net weight 20kg/drum, easy to transport and store.
This product is non-dangerous, please store it away from fire sources and strong oxidants.