PFA Pellet SF-3304A with MFR 12.1-16
Product Description
PFA is the copolymer of TFE and PPVE, with excellent chemical stability. electrical insulating property, age resistance and low friction. Its high temperature mechanical property is much higher than PTFE and can be processed as common thermoplastics.
Grades and Technical Properties
| Item | Unit | SF3301 | SF3302 | SF3303 | SF3304 | ||
| A | B | C | |||||
| Appearance | Translucent particle, without impurities such as metal debris and sand, containing visible black particles percentage point less than 6% | ||||||
| MFR | g/10min | 0.8-2.5 | 2.6-6 | 6.1-12 | 12.1-16 | 16.1-24 | ＞24.1 |
| Relative Gravity(25℃) | g/cm3 | 2.12-2.17 | |||||
| Melting Point | ℃ | 300-310 | |||||
| Processing Tm | ℃ | 260 | |||||
| Tensile Strength(23℃),≥ | MPa | 32 | 30 | 28 | 26 | 24 | 24 |
| Elongation at break(23℃),≥ | % | 300 | 300 | 350 | 350 | 350 | 350 |
| Volatile,＜ | ％ | 0.01 | |||||
Application:
SF3301: used to produce lining of pipe, valve, pump and bearing;
SF3302:used to produce pipe, insulation jacket of wire, membranes;
SF3303:extrusion process, mainly used to produce the jackets of wire and cable;
SF3304:used to produce high-speed extruded wire and cable.
Attention
The process temperature should not exceed 425℃ to prevent PFA decomposition and equipment corrosion.3. Product waste must be handled properly following local laws and regulations.
Packaging, Storage and Transportation
1.Packing:in woven plastic bag with inner polyethylene bag of 25kgs net.
2.Stored in clean, cool and dry places to avoid contamination.
3.Nontoxic, noninflammable, inexplosive, non-corrosion, transported as non-dangerous products.